[en] Free-radical-initiated grafting of maleic anhydride (MA) onto poly(butylene adipate-co-terephthalate) (PBAT), a biodegradable aliphatic-aromatic copolyester, was performed by reactive extrusion. 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane was used as the free-radical initiator. The peroxide concentration was varied between 0.0 and 0.5 wt % at 3.0 wt % MA concentration; the MA concentration was varied between 1.0 and 5.0 wt % at 0.5 wt % peroxide concentration. The reaction temperature was maintained at 185 °C for all experiments. Under these conditions, between 0.194% and 0.691% MA was grafted onto the polyester backbone. Size-exclusion chromatography, melt flow index, intrinsic viscosity measurements, thermal gravimetric analysis, and differential scanning calorimetry were used to characterize the maleated copolyester. Increasing the initiator concentration at a constant MA concentration of 3% resulted in an increase in the grafting of MA while decreasing the molecular weight of the resulting polymer. Increasing the feed MA concentration also increased the grafting percentage. The maleation of the polyester proved to be very efficient in promoting strong interfacial adhesion with high amylose cornstarch in starch foams as prepared by melt blending. Thus, the use of maleated copolyester as a compatibilizer between starch and PBAT allowed the reduction of the density of resulting starch foams to 21 kg/m3 and improved the resilience from 84% to as high as 95%. Also, the resulting starch foams exhibited improved hydrophobic properties in terms of lower weight gain and higher dimensional stability on moisture sorption.
Rowell, P.; Schultz, T.; Narayan, R. Emerging Technologies for Materials and Chemicals from Biomass; ACS Symposium Series 467; American Chemical Society: Washington, DC, 1991.
Narayan, R. Polymeric Materials from Agricultural Feedstocks. In Polymers from Agricultural Coproducts; Fishman, M. L., Friedman, R. B., Huang, S. J., Eds.; ACS Symposium Series 575; American Chemical Society: Washington, DC, 1994; p 2.
Narayan, R. Commercialization Technology: "A Case Study of Starch Based Biodegradable Plastics". In Paradigm for Successfull Utilization of Renewable Resources; Sessa, D. J., Willett, J. L., Eds.; AOCS Press: Champaign, IL, 1998; p 78.
Lacourse, N. L.; Altieri, P. A. U.S. Patent 4,863,655, 1989.
Lacourse, N. L.; Altieri, P. A. U.S. Patent 5,043,196, 1991.
Chinnaswamy, R.; Hanna, M. A. U.S. Patent 5,496,895, 1996.
Chinnaswamy, R.; Hanna, M. A. Australian Patent AU-B-63333/90, 1996.
Bhatnagar, S.; Hanna, M. A. Trans. ASAE 1995, 38, 567.
Cha, J. Y.; Chung, D. S.; Seib, P. A.; Flores, R. A.; Hanna, M. A. Ind. Crops Prod. 2001, 14, 23.
Cha, J. Y.; Chung, D. S.; Seib, P. A. Trans. ASAE 1999, 42, 1765.
Cha, J. Y.; Chung, D. S.; Seib, P. A. Trans. ASAE 1999, 42, 1801.
Boehmer, E. W., Hanlon, D. L. U.S. Patent 5,272,181, 1993.
Altieri, P. A.; Tessler, M. M. U.S. Patent 5,554,660, 1996.
Bastioli, C.; Bellotti, V.; Del Giudice, L.; Lombi, R.; Rallis, A.; Del Tredici, G.; Montino, A.; Ponti, R. U.S. Patent 5,288,765, 1994.
Bastioli, C.; Bellotti, V.; Del Giudice, L.; Lombi, R.; Rallis, A. U.S. Patent 5,360,830, 1994.
Bastioli, C.; Bellotti, V.; Del Tredici, G.; Montino, A.; Ponti, R. U.S. Patent 5,736,586, 1998.
Bastioli, C.; Bellotti, V.; Del Tredici, G.; Rallis, A. U.S. Patent 5,801,207, 1998.
Neumann, P. E.; Seib, P. A. U.S. Patent 5,185,382, 1993.
Neumann, P. E.; Seib, P. A. U.S. Patent 5,208,267, 1993.
Xu, W.; Doane, W. M. U.S. Patent 5,665,786, 1997.
Xu, W.; Doane, W. M. U.S. Patent 5,854,345, 1998.
Shogren, R. L. Carbohydr. Polym. 1996, 29 (1), 57-62.
Wang, L.; Shogren, R. L. Proceedings 6th Annual Meeting of the Bio/Environmental Degradable Polymer Society; The Society: St. Paul, MN, 1997.
Fang, Q.; Hanna, M. A. Cereal Chem. 2000, 77 (6), 779-783.
Fang, Q.; Hanna, M. A. Bioresour. Technol. 2001, 78, 115-122.
Biby, G.; Hanna, M. A.; Fang, Q. U.S. Patent 6,184,261, 2001.
Fang, Q.; Hanna, M. A. Ind. Crops Prod. 2001, 13, 219-227.
Willett, J. L.; Shogren, R. L. Polymer 2002, 43, 5935-5947.
Barlow, J. W.; Paul, D. R. Polym. Eng. Sci. 1984, 24, 525-534.
Ruggeri, G.; Aglietto, M.; Petramani A.; Ciardelli, F. Eur. Polym. J. 1983, 19, 863-866.
Bratawidjaja, A. S.; Gitopadmoyo, I.; Watanabe, Y.; Hatakeyama, T. J. Appl. Polym. Sci. 1989, 37, 1141-1145.
Ho, R. M.; Su, A. C.; Wu, C. H.; Chen, S. I. Polymer 1993, 34, 3264-3269.
Rengarajan, R.; Parameshwar, V. R.; Lee, S.; Rinaldi, P. L. Polymer 1990, 31, 1703-1706.
Singh, R. P. Prog. Polym. Sci. 1992, 17, 251-281.
Minoura, Y.; Ueda, M.; Mizunuma, S.; Oba, M. J. Appl. Polym. Sci. 1969, 13, 1625-1640.
Vijayakumar, M. T.; Reddy, C. R.; Joseph, K. T. Eur. Polym. J. 1985, 21, 415-419.
Grigo, U.; Merten, J.; Binsack, R. U.S. Patent 4,370,450, 1983.
Rengarajan, R.; Vicic, M.; Lee, S. Polymer 1989, 30, 933-935.
Doane, W. M.; Swanson, C. L.; Fanta, G. F. In Emerging Technologies for Materials and Chemicals from Biomass; ACS Symposium Series 476; Rowell, R. M., Schultz, T. P., Narayan, R., Eds; American Chemical Society: Washington, DC, 1992; p 197.
Glassner, W. G. In Wood Processing and Utilization; Kennedy, J. F., Phillips, G. O., Williams, P. A., Eds; Ellis Horwood Ltd.: West Sussex, U.K., 1989; p 163.
Sathe, S. N.; Rao, G. S. S.; Devi, S. J. Appl. Polym. Sci. 1994, 53, 239-245.
Vermesch, L.; Groeninckx, G. J. Appl. Polym. Sci. 1994, 53, 1365-1373.
Vaidya, U. R.; Bhattacharya, M. J. Appl. Polym. Sci. 1994, 52, 617-628.
Vaidya, U. R.; Bhattacharya, M.; Zhang, D. Polymer 1995, 36, 1179-1188.
Bhattacharya, M.; Vaidya, U. R.; Zhang, D.; Narayan, R. J. Appl. Polym. Sci. 1995, 57, 539-554.
Ramkumar, D. H. S.; Bhattacharya, M.; Vaidya, U. R.; Hakkainen, M.; Albertsson, A. C.; Karlsson, S. Eur. Polym. J. 1996, 32, 999-1010.
Ramkumar, D. H. S.; Bhattacharya, M.; Vaidya, U. R. Eur. Polym. J. 1997, 33, 729-742.
John, J.; Tang, J.; Yang, Z.; Bhattacharya, M. J. Polym. Sci., Part A: Polym. Chem 1997, 35, 1139-1148.
Mani, R.; Bhattacharya, M. Eur. Polym. J. 1998, 34, 1467-1475.
Mani, R.; Bhattacharya, M. Eur. Polym. J. 1998, 34, 1477-1487.
American Standard Test Methods, 2002. Standard Test Method for Melt Flow Rates of Thermoplastics by Extrusion Plastometer. In Annual Book of ASTM Standards; D-1238, 08.01; ASTM: Philadelphia, PA, 2002.
American Standard Test Methods, 2002. Standard Practice for Conditioning Containers, Packages, or Packaging Components for Testing. In Annual Book of ASTM Standards; D-4332, 15.09; ASTM: Philadelphia, PA, 2002.
American Standard Test Methods, 2002. Standard Test Methods for Flexible Cellular Materials Made From Olefin Polymers. In Annual Book of ASTM Standards; D-3575, 08.02; ASTM: Philadelphia, PA, 2002.
Tatarka, P. D.; Cunningham, R. L. J. Appl. Polym. Sci. 1998, 67, 1157-1176.
Bellamy, L. J. The Infra-Red Spectra of Complex Molecules Wiley: New York, 1964.
Pouchert, C. J. The Aldrich Library of Infra-Red Spectra Aldrich Chemical Co.: Milwaukee, WI, 1970.
Hutchinson, R. J.; Siodlak, G. D. E.; Smith, A. C. J. Mater. Sci. 1987, 22, 3956-3962.
Biresaw, G.; Carriere, C. J. J. Polym. Sci., Part B: Polym. Phys. 2000, 39, 920-930.
Lawton, J. W. Biodegradable Coatings for Thermoplastic Starch. In Cereal: Novel Uses and Processes; Campbell, G. M., Webb, C., McKee, S. L., Eds.; Plenum Press: New York, 1997; p 43.
Walia, P. S.; Lawton, J. W.; Shogren, R. L.; Felker, F. C. Polymer 2000, 41, 8083-8093.
Averous, L.; Fauconnier, N.; Moro, L.; Fringant, C. J. Appl. Polym. Sci. 2000, 76, 1117-1128.